Features & Benefits
- Fast Setting Self Curing Resin
- Self-Curing Acrylic Resin RE-FINE BRIGHT by Yamahachi
- Increased resistance to tarnishing, conventional problems of yellow discoloration avoided and transparency retained.
- High strengthening resin. Component particles are of various sizes, strengthening, bonding and enhancing other physical properties.
- Superior shaving and cutting possible. Desired cutting feasible as the revolutions of bars and points are uninhibited.
- Enhanced operation. Exceptional mixing ability of the powder and liquid results in accurate reproductions.
Physical Properties
Powder/Liquid Mixing Ratio, g:m | 1 : 0.5 |
---|---|
*Hardening Time (23℃) | 3min 30sec |
Working Time | 1min |
Flexural Strength, MPa | 75 |
Flexural Modulus, MPa | 1,517 |
Vickers Hardness, Hv | 11.4 |
Sorption, μg/mm3 | 16 |
Solubility, μg/mm3 | 2.2 |
Residual Monomer, wt% | 3.3 |
* Hardening time value using prescribed powder/liquid mixing ratio at 23℃.
Hardening time at lower and higher room temperature will become longer and shorter, respectively.